Routine aluminium hydroxide(Aluminium hydroxide flame redirtant)
Aluminum hydroxide nigicuruzwa cyera. Isura yayo ni ifu yera ya kirindwi, idafite uburozi kandi idafite impumuro nziza, imbwa nziza, umweru muremure, igikundiro gito. Ni ikigo cya amphoteric. Ibirimo nyamukuru ni al (OH)3.
- Aluminium hydroxideirinda kunywa itabi. Ntabwo ikora nta miti itonyanga na gaze yubumara. Ni labile mu gisubizo gikomeye cya alkali na acide ikomeye. Ihinduka Alumina nyuma ya Pyrolysis no kubura umwuma, hamwe nabatari uburozi kandi bafite impumuro.
- Ibikorwa bya Aluminum bikora byakozwe nikoranabuhanga rigezweho, hamwe nuburyo butandukanye bwo guhinduranya hamwe nabakozi baho bahuza imitungo yo kuvura hejuru.
Gusaba:
Ikoreshwa nkibikoresho muburyo butandukanye bwa aluminide, nkumukozi witabarwa muri plastiki, inganda za latex.Ni uSed Mumpapuro Gukora Impapuro, Gushushanya, amenyo, amenyo, pigment, umukozi wumisha, inganda za farumasikandiAchate.
Ikoraaluminium hydroxideikoreshwa muri plastiki, inganda za reberi. Ikoreshwa cyane mu mashanyarazi, ibyuma bya reberi, nk'ikibaya cyo kwigarurira insinga n'amashanyarazi n'umugozi, adiabator, umukandara wa conposition.
Ipaki:40 kg yoha igikapu hamwe na pe imbere.
Ubwikorezi:Nibicuruzwa bitari uburozi. Ntukavunike paki mugihe cyo gutwara, kandi wirinde ubuhehere kandiamazi.
Ububiko:Ahantu humye kandi guhumeka.
Inganda za tekiniki:
| Ibisobanuro | Ibigize imiti% | PH | Kwinjiza peteroli ml / 100g≤ | Whiteney ≥ | Amanota | Umugereka wamazi% ≤ | |||||
| Al (Oh)3≥ | Sio2≤ | Fe2O3≤ | Na2O | Ingano yo hagati D50 μm | 100% | 325% | |||||
| H-wf-1 | 99.5 | 0.08 | 0.02 | 0.3 | 7.5-9.8 | 55 | 97 | ≤1 | 0 | ≤0.1 | 0.5 |
| H-wf-2 | 99.5 | 0.08 | 0.02 | 0.4 | 50 | 96 | 1-3 | 0 | ≤0.1 | 0.5 | |
| H-wf-5 | 99.6 | 0.05 | 0.02 | 0.25 | 40 | 96 | 3-6 | 0 | ≤1 | 0.4 | |
| H-wf-7 | 99.6 | 0.05 | 0.02 | 0.3 | 35 | 96 | 6-8 | 0 | ≤3 | 0.4 | |
| H-wf-8 | 99.6 | 0.05 | 0.02 | 0.3 | 33 | 96 | 7-9 | 0 | ≤3 | 0.4 | |
| H-WF-10 | 99.6 | 0.05 | 0.02 | 0.3 | 33 | 96 | 8-11 | 0 | ≤4 | 0.3 | |
| H-wf-10-ls | 99.6 | 0.05 | 0.02 | 0.2 | 33 | 96 | 8-11 | 0 | ≤4 | 0.3 | |
| H-wf-10-sp | 99.6 | 0.03 | 0.02 | 0.2 | 7.5-9.0 | 32 | 95 | 8-11 | 0 | ≤4 | 0.3 |
| H-wf-12 | 99.6 | 0.05 | 0.02 | 0.3 | 32 | 95 | 10-13 | 0 | ≤5 | 0.3 | |
| H-wf-14 | 99.6 | 0.05 | 0.02 | 0.3 | 32 | 95 | 13-18 | 0 | ≤12 | 0.3 | |
| H-wf-14-sp | 99.6 | 0.03 | 0.02 | 0.2 | 30 | 95 | 13-18 | 0 | ≤12 | 0.3 | |
| H-wf-20 | 99.6 | 0.05 | 0.02 | 0.25 | 7.5-9.8 | 32 | 95 | 18-25 | 0 | ≤30 | 0.2 |
| H-wf-20-sp | 99.6 | 0.03 | 0.02 | 0.2 | 7.5-9.8 | 30 | 94 | 18-25 | 0 | ≤30 | 0.2 |
| H-wf-25 | 99.6 | 0.05 | 0.02 | 0.3 | 32 | 95 | 22-28 | 0 | ≤35 | 0.2 | |
| H-wf-40 | 99.6 | 0.05 | 0.02 | 0.2 | 33 | 95 | 35-45 | 0 | - | 0.2 | |
| H-wf-50-sp | 99.6 | 0.03 | 0.02 | 0.2 | 7.5-10 | 30 | 93 | 40-60 | 0 | - | 0.2 |
| H-wf-60-sp | 99.6 | 0.03 | 0.02 | 0.2 | 30 | 92 | 50-70 | 0 | - | 0.1 | |
| H-wf-75 | 99.6 | 0.05 | 0.02 | 0.2 | 40 | 93 | 75-90 | 0 | - | 0.1 | |
| H-wf-75-sp | 99.6 | 0.03 | 0.02 | 0.2 | 30 | 92 | 75-90 | 0 | - | 0.1 | |
| H-wf-90 | 99.6 | 0.05 | 0.02 | 0.2 | 40 | 93 | 70-100 | 0 | - | 0.1 | |
| H-wf-90-sp | 99.6 | 0.03 | 0.02 | 0.2 | 30 | 91 | 80-100 | 0 | - | 0.1 | |